Edelstahl-Spindelwelle — hartgedreht auf Ra 0,2 µm
Eine 17-4PH-Spindelwelle, im Zustand H900 hartgedreht, mit Ra 0,2 µm am Dichtdurchmesser — ganz ohne Schleifoperation.
Bauteildaten
- Branche
- Energy, Oil & Gas
- Verfahren
- CNC Turning
- Werkstoff
- Stainless 17-4PH H900
- Toleranz
- ±0.005 mm
- Oberfläche
- Superfinished, Ra 0.2 µm
- Stückzahl
- 300 / year
- Lieferzeit
- 19 working days
Kundendaten aufgrund eines NDA nicht genannt.
Herausforderung
The shaft runs a lip seal at 6,000 rpm. The specification called for Ra 0.2 µm with no circumferential lay, which normally implies plunge grinding followed by superfinishing — two operations and a subcontract step.
Lösung
We hard-turned the sealing diameter after age-hardening, using a CBN insert at high surface speed with a small nose radius and very low feed. A superfinishing belt pass removes the residual turning lay and brings the surface to a non-directional finish.
Ergebnis
Ra measures 0.16 – 0.19 µm with no measurable lay, meeting the seal manufacturer's requirement. The grinding subcontract was eliminated, cutting five days from the lead time and 21 % from the unit cost.