Arbre de broche inox — tourné dur à Ra 0,2 µm
Un arbre de broche en 17-4PH tourné dur à l'état H900, atteignant Ra 0,2 µm sur le diamètre d'étanchéité sans opération de rectification.
Spécification de la pièce
- Secteur
- Energy, Oil & Gas
- Procédé
- CNC Turning
- Matière
- Stainless 17-4PH H900
- Tolérance
- ±0.005 mm
- Finition
- Superfinished, Ra 0.2 µm
- Quantité
- 300 / year
- Délai
- 19 working days
Identité du client non divulguée (NDA).
Problématique
The shaft runs a lip seal at 6,000 rpm. The specification called for Ra 0.2 µm with no circumferential lay, which normally implies plunge grinding followed by superfinishing — two operations and a subcontract step.
Solution
We hard-turned the sealing diameter after age-hardening, using a CBN insert at high surface speed with a small nose radius and very low feed. A superfinishing belt pass removes the residual turning lay and brings the surface to a non-directional finish.
Résultat
Ra measures 0.16 – 0.19 µm with no measurable lay, meeting the seal manufacturer's requirement. The grinding subcontract was eliminated, cutting five days from the lead time and 21 % from the unit cost.